  The influence of reinforcement morphology on damage tolerance and fracture toughness of epoxy based nanocomposites has been studied. Two different forms of carbonaceous reinforcements were used: multi-layered graphene (MLG) and nanostructured graphite (NSG). The maximum increase in Young's modulus was observed from 609.6 MPa to 766 MPa (25.7% increase) in the case of 0.1 wt% NSG. The NSG showed a maximum increase in hardness up to 7.9% while MLG showed up to 18.3%. The MLG and NSG increased the storage modulus and Tg while loss modulus and tan δ decreased with MLG and NSG. SEM images of the fractured surfaces of tensile specimens showed that the fracture mode was significantly altered by MLG and NSG.